Af=55''C Ni 50.2% Niinol Bar & Rods
Next product
0.12mm nitinol foil
Click to enlarge

Atom %Ni- 50.0-50.2 Nitinol Bars

Product Detail
1.High temperature Nitinol Bar

2.Dia6.0~45mm x L

3.Af=55’C, 65’C, 80’C~110’C

4.Smooth surface

5.For industry used

High Temperature Large Nitinol bars

1.The reverse martensitic transformation Af=  55’C+/-5, 65’C+/-5, 80’C+/-5 , 110’C+/-‘C

  1. Atom %Ni – 50.0-50.2
    Mass %Ni – 54.9-55.1
    Balance – Ti
    In the aggregate 100%
    Base impurity (O, C, N, H) content must be less then 0,25%
  1. -Material test certificates offered according the standard EN 10204 B3.1
  2. Application: Industrial, Medical, Chemistry, Aerospace, Military etc.
  3. Test & Quality:

-a. ISO 9001:2008

-b. Mill test report Provided

-c. Third Party Inspection

Category: Tags: , , ,
Description

Description

Product Detail
1.High temperature Nitinol Bar

2.Dia6.0~45mm x L

3.Af=55’C, 65’C, 80’C~110’C

4.Smooth surface

5.For industry used

High Temperature Large Nitinol bars

1.The reverse martensitic transformation Af=  55’C+/-5, 65’C+/-5, 80’C+/-5 , 110’C+/-‘C

  1. Atom %Ni – 50.0-50.2
    Mass %Ni – 54.9-55.1
    Balance – Ti
    In the aggregate 100%
    Base impurity (O, C, N, H) content must be less then 0,25%
  1. -Material test certificates offered according the standard EN 10204 B3.1
  2. Application: Industrial, Medical, Chemistry, Aerospace, Military etc.
  3. Test & Quality:

-a. ISO 9001:2008

-b. Mill test report Provided

-c. Third Party Inspection

Shipping & Delivery

Vestibulum curae torquent diam diam commodo parturient penatibus nunc dui adipiscing convallis bulum parturient suspendisse parturient a.Parturient in parturient scelerisque nibh lectus quam a natoque adipiscing a vestibulum hendrerit et pharetra fames.Consequat net

Vestibulum parturient suspendisse parturient a.Parturient in parturient scelerisque nibh lectus quam a natoque adipiscing a vestibulum hendrerit et pharetra fames.Consequat netus.

Scelerisque adipiscing bibendum sem vestibulum et in a a a purus lectus faucibus lobortis tincidunt purus lectus nisl class eros.Condimentum a et ullamcorper dictumst mus et tristique elementum nam inceptos hac vestibulum amet elit